S235JR Galvanized steel pipe

S235JR Galvanized steel pipe
ot dip galvanized pipe is to make molten metal and iron matrix reaction to produce an alloy layer, so that the matrix and coating are combined. Hot dip galvanized steel pipe is first pickling, in order to remove iron oxide on the surface of the steel pipe, after pickling, through ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank for cleaning, and then into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. Hot dip galvanized steel tube matrix and molten bath have complex physical and chemical reactions, forming corrosion resistant structure of tight zinc-iron alloy layer. The alloy layer is integrated with pure zinc layer and steel tube matrix, so it has strong corrosion resistance.

Special specifications can be customized according to customer requirements, please contact us to explain separately!

Contact us

PRODUCT DETELS

Chemical composition:

BrandCMnSiPS
Q235A≤0.22≤1.4≤0.35≤0.0500.045
Q235B≤0.20≤1.4≤0.35≤0.0500.045
Q235C≤0.17≤1.4≤0.35≤0.0500.045
Q235D≤0.17≤1.4≤0.35≤0.0500.045


BrandTensile strength (MPA)kg/mm²Yield strength (MPA)kg/mm²Elongation δ (%)
Q235AQ235BQ235CQ235D375-500235≥26(a≤16mm)≥25(a>16-40mm)≥24(a>40-60mm)≥23(a>60-100mm)≥22(a>100-150mm)≥21(a>150mm)

Standards: JIS G3302, ASTM A653M, EN10327, DIN 17162, EN 10142, EN 10147, EN 10292, JIS G3302

Material: DX51D+Z, DX52D+Z, DX53D+Z, DX54D+Z, S220GD+Z, DX51D+Z/SGCC/A653, etc

Zinc Coating: 40-600g/㎡

Width: 1000mm, 1219mm, 1250mm, 1500mm or customized as required

Thickness: 0.1-6.5mm or customized as required

Surface Finish: Regular spangle, Big spangle, minimum spangle, zero spangle


展示.gif

Hot dip galvanized pipe

Hot dip galvanized pipe is to make molten metal and iron matrix reaction to produce an alloy layer, so that the matrix and coating are combined. Hot dip galvanized steel pipe is first pickling, in order to remove iron oxide on the surface of the steel pipe, after pickling, through ammonium chloride or zinc chloride aqueous solution or ammonium chloride and zinc chloride mixed aqueous solution tank for cleaning, and then into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life. Hot dip galvanized steel tube matrix and molten bath have complex physical and chemical reactions, forming corrosion resistant structure of tight zinc-iron alloy layer. The alloy layer is integrated with pure zinc layer and steel tube matrix, so it has strong corrosion resistance.


Cold galvanized pipe

Cold galvanized pipe is electric galvanized, galvanized amount is very little, only 10-50g/m2, its own corrosion resistance is much different than hot galvanized pipe. Regular galvanized pipe manufacturers, in order to ensure quality, most do not use galvanized (cold plating). Only those small enterprises with obsolete equipment use electrogalvanizing, of course, their price is relatively cheaper. The Ministry of Construction has officially below, the elimination of cold galvanized pipe technology behind, not allowed to use cold galvanized pipe for water, gas pipe. The galvanized layer of cold galvanized steel pipe is an electric coating, and the zinc layer is independently layered with the steel pipe matrix. The zinc layer is thin, and the zinc layer is simply attached to the steel tube matrix and easy to fall off. Therefore, its corrosion resistance is poor. In new residential buildings, it is forbidden to use cold galvanized steel pipes as water supply pipes.